CATALYTIC EFFECTS OF FERROCENE ON BONDING, OPTICAL AND STRUCTURAL PROPERTIES OF DIAMOND-LIKE CARBON FILMS DEPOSITED BY MICROWAVE SURFACE-WAVE PLASMA CHEMICAL VAPOR DEPOSITION.

This paper reports catalytic effects of ferrocene on bonding, optical and structural properties of diamond-like carbon (DLC) thin films grown on silicon and quartz substrates by microwave surface-wave plasma chemical vapor deposition. For film deposition, helium and methane gases were used as plasma source. Bonding, optical and structural properties of the DLC films were measured both with and without using ferrocene as a catalyst. The ferrocene content in the DLC was confirmed by X-ray spectroscopy (XPS) measurement. The optical band gap decreased from 2.7 eV (without ferrocene) to 1.6 eV (with ferrocene). Raman spectra of the ferrocene content film shows that the G-peak was more pronounced compared to the film without ferrocene. Results suggest that appropriate concentration of ferrocene in DLC film helps to reduce the optical band gap because of ferrocene-induced graphitization. [ABSTRACT FROM AUTHOR]

Copyright of Surface Review & Letters is the property of World Scientific Publishing Company and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)