Investigation of Biofilm Formation on Air Cathodes with Quaternary Ammonium Compounds in Microbial Fuel Cells.

The use of gas diffusion electrodes (GDEs) in microbial fuel cells (MFCs) can improve their cell performance, but tends to cause fouling. In order to allow long-term stable operation, the search for antifouling methods is necessary. Therefore, an antibacterial coating with ammonium compounds is investigated. Within the first 30 days of operation, the maximum measured power density of a GDE with antibacterial ionomer was 606 mW m⁻². The GDE without an antifouling treatment could only reach a maximum of 284 mW m⁻². Furthermore, there was an optimum in the loading amount with ionomer below 2.6 mg cm⁻². Further investigations showed that additional aeration of the GDEs by a fan had a negative effect on their performance. Despite the higher performance, the antibacterial coating could not prevent biofilm growth at the surface of the GDE. The thickness of the biofilm was only reduced by 14–16%. However, the weight of the biofilm on the treated GDEs was 62–80% less than on a GDE without an antifouling treatment. Consequently, the coating cannot completely prevent fouling, but possibly leads to a lower density of the biofilm or prevents clogging of the pores inside the electrodes and improves their long-term stability. [ABSTRACT FROM AUTHOR]

Copyright of Fermentation (Basel) is the property of MDPI and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)