High Performance Dental Zirconia Ceramics Fabricated by Vat Photopolymerization Based on Aqueous Suspension.

Currently, a significant challenge in the fabrication of ceramic dental prostheses via vat photopolymerization lies in the utilization of slurries composed of organic monomers, which compromises environmental sustainability and impedes commercial viability. In this research, we successfully develop a low-viscosity aqueous zirconia ceramic suspension with a solid loading of 40 vol% and 20 vol% deionized waters, incorporating 3 wt% dispersant and 0.5 wt% photoinitiator for printing dental crowns using vat photopolymerization. The resulting green bodies require only water washing to remove unreacted material. The printed ceramics demonstrate an average flexural strength of 708 MPa, a relative density of 98.3 %, and a Vickers hardness of 14.7 GPa. A dental crown is ultimately fabricated with an accuracy of 92.8 %. This study demonstrates that zirconia ceramics fabricated by vat photopolymerization with aqueous suspension exhibit excellent mechanical properties and accuracy, highlighting their potential for broad applications in dental restorations through an environmentally sustainable approach. [ABSTRACT FROM AUTHOR]

Copyright of Journal of the European Ceramic Society is the property of Elsevier B.V. and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)