Selective Electrochemical CO2 Reduction tuned by N Configuration on graphitic Shells of Nickel Particles.

Despite of high conductivity and reducing ability, transition metal nanoparticles tend to aggregate and unavoidably impact the selectivity during the proton‐coupled reduction process of CO2RR. New strategy to regulate and utilize the electronic property of transition‐metal particles allows for effective tuning of eCO2RR activity. Through simple creation of N‐doped carbon shells surrounding Ni nanoparticles and controlling the amount and arrangement of the N atoms, successful and long‐lasting electrochemical reduction of CO2 was accomplished. The inherent HER activity was almost completely suppressed. It exhibited FECO above 90 % in a 500 mV potential window, with the optimal up to 96.5 % at −0.78 V vs RHE. In flow cell electrolysis, a current density of 289.4 mA/cm2 was achieved with Faradic efficiency of 96.4 % towards CO. The results of control experiments using different catalysts imply that electron transfer between Ni core and shells was significantly influenced by the property of N atoms. High content of graphitic nitrogen is crucial for the catalytic performance. [ABSTRACT FROM AUTHOR]

Copyright of ChemistrySelect is the property of Wiley-Blackwell and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)