Alterations in Surface Gloss and Hardness of Direct Dental Resin Composites and Indirect CAD/CAM Composite Block after Single Application of Bifluorid 10 Varnish: An In Vitro Study.

The surface characteristics of the restorative material are essential to its longevity. Since resin composites are polymeric-based materials, they could be degraded when exposed to oral conditions and chemical treatment. Certain chemical solutions, such as fluoride varnish, have the potential to deteriorate the resin composite's surface properties such as gloss and hardness. The current study aimed to assess and compare the surface gloss and hardness of different types of dental resin composites (nanohybrid, ormocer, bulk-fill flowable direct composites, and indirect CAD/CAM resin composite blocks (BreCAM.HIPC)) after a single application of Bifluorid 10 varnish. A total of 80 disc-shaped resin composite specimens were evenly distributed in four groups of 20 specimens. These were divided into two equal subgroups of specimens with topical fluoride (TF) application (n = 10) and without TF application (n = 10). The specimens were examined for surface gloss and hardness. Independent sample t-test was used to investigate statistically the effect of TF on the gloss as well as the hardness of each material. One-way ANOVA and post hoc tests were used to assess the difference in gloss and hardness among the materials without and with TF application. The significance level was adjusted to p ≤ 0.05. The results of gloss showed that the TF application led to a significant reduction in gloss values of all tested composites. The gloss among the various materials was significantly different. The TF had no significant effect on the hardness of nanohybrid, bulk-fill flowable, and BreCAM.HIPC composites (p = 0.8, 0.6, and 0.3, respectively). On the other hand, the hardness of ormocer was significantly reduced after TF application. Comparing the different resin composite materials, the hardness significantly differed. This study concluded that surface gloss and hardness seem to be impacted by the type and composition of the resin composites and vary depending on fluoride application. [ABSTRACT FROM AUTHOR]

Copyright of Journal of Composites Science is the property of MDPI and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)