Nonisothermal crystallization kinetic behavior of pure ethylene-Vinyl acetate copolymers and ethylene-Vinyl acetate copolymer/nitrile rubber thermoplastic vulcanizate.

Item request has been placed! ×
Item request cannot be made. ×
loading   Processing Request
Read More Add to Saved list
  • Additional Information
    • Subject Terms:
      CRYSTALLIZATION kinetics; NITRILE rubber; THERMOPLASTIC elastomers; ETHYLENE-vinyl acetate; CRYSTALLIZATION; CRYSTAL growth
    • Abstract:
      Thermoplastic vulcanizate (TPV) made from the ethylene-vinyl acetate copolymer (EVA)/nitrile rubber (NBR) blend was fabricated using the dynamic vulcanization method. Differential scanning calorimetry (DSC) was utilized to analyze the nonisothermal crystallization kinetics of both pure EVA and EVA/NBR TPV. The nonisothermal crystallization mechanism was evaluated using the Avrami method modified by Jeziorny, the Ozawa method and the Mo method. The results demonstrate that the nonisothermal crystallization of both pure EVA and EVA/NBR TPV can be adequately described by the Avrami method modified by Jeziorny and the Mo method, while the Ozawa method is not applicable. By elevating the cooling rate, there was a reduction in the crystallization temperature and t1/2 for both pure EVA and EVA/NBR TPV, while the degree of crystallization increased. At the same cooling rate, the crystallization temperature of the EVA/NBR TPV was found to be higher than that of the pure EVA, suggesting that the presence of NBR facilitated the nucleation of the EVA matrix within the EVA/NBR TPV. Moreover, a steric hindrance effect existed in the NBR phase of EVA/NBR TPV at the same cooling rate, resulting in a larger t 1/2 compared to that of the pure EVA, indicating hindered crystal growth. [ABSTRACT FROM AUTHOR]
    • Abstract:
      Copyright of Journal of Thermoplastic Composite Materials is the property of Sage Publications Inc. and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)