Photothermal superhydrophobic surface with good corrosion resistance, anti-/de-icing property and mechanical robustness fabricated via multiple-pulse laser ablation.

Item request has been placed! ×
Item request cannot be made. ×
loading   Processing Request
  • Additional Information
    • Abstract:
      [Display omitted] • A black superhydrophobic surface was fabricated on steel substrate via an eco-friendly multiple-pulse laser ablation method. • The surface has good corrosion resistance with a 64.78-times lower corrosion current density than steel substrate. • The surface exhibit excellent anti-/de-icing property with longer freezing delay time and shorter photothermal de-icing time than steel substrate. • The surface is of good mechanical robustness, it can keep superhydrophobicity after impacting by 2000 g of sands or 400 times of tape peeling tests. Corrosion and ice accumulation occurring on carbon steel bring about huge economy lost, resource waste, and even hazard event. Fabricating black superhydrophobic surfaces is an effective method for improving the anti-corrosion and anti-/de-icing properties of metallic materials. However, it is still a challengeable task to fabricate a robust black superhydrophobic surface on carbon steel through an eco-friendly method. Herein, a black superhydrophobic surface was obtained on 45 steel substrate via a simple and fluorine-free method, i.e., multiple-pulse laser ablation followed by chemical modification with hexadecyltrimethoxysilane (HDTMS). The obtained surface exhibits a water contact angle of 156° and possesses a low reflectance (<9%) in the wavelength range of 400 ∼ 2500 nm. The surface displays an excellent photothermal property with a temperature rise of 52 °C under 1 sun of illumination within 8 min. Electrochemistry data reveals that the surface has good corrosion resistance with 64.78-times lower corrosion current density and 73.81-times higher charge transfer resistance than the steel substrate. Anti-icing test shows that the surface possesses 2547 s longer freezing delay time and at least ∼ 3 times lower de-icing force than the steel substrate, and photothermal de-icing test demonstrates that the ice on the surfaces starts thawing within 60 s under 0.5 sun of illumination, indicating that the surface has excellent anti-/de-icing property. Moreover, after impacting by 2000 g of sands or 400 times of tape peeling tests, the surface still maintains superhydrophobicity, indicating the good mechanical robustness of the surface. [ABSTRACT FROM AUTHOR]
    • Abstract:
      Copyright of Applied Surface Science is the property of Elsevier B.V. and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)