Synthesis and thermal characterization of composites based on Epidian 601 with flame retardants compounds.

This study presents the preparation and flammability characteristics of polymeric composites based on the epoxy resin Epidian® 601. The triethylenetetramine (TETA) and commercial curing agents based on polyamines (IDA and PAC) were used as crosslinking compounds. Moreover, two flame retardant compounds were added to this composition, the commercial Fire Retardant (FR) and triphenyl phosphate (TP). The chemical structure of the composites and the course of curing processes were confirmed by the ATR/FT-IR (Attenuated Total Reflection–Fourier Transform Infrared) analysis. The influence of different amounts of FR or TP on the flammability and thermal resistance was discussed in detail. After the flammability test the samples were also studied to assess their thermal destruction. In addition, the composites were subjected to the swelling tests, solvent resistance, and microscopic observations. The DSC curves revealed that all materials were characterized by good thermal properties. All materials were temperature resistant up to 300 °C. Furthermore, the measurements of the hardness of the composite demonstrated that the material EP601 + TETA + 10 %FR is the hardest. The addition of FR and RP influenced the flammability of the composites increasing the thermal resistance. The ageing tests in methanol, acetone, hydrochloric acid, and potassium hydroxide were also carried out. [ABSTRACT FROM AUTHOR]

Copyright of Pure & Applied Chemistry is the property of De Gruyter and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)