Comparing the bond strength of fiber post cementation in the root canal using pre- and co-curing procedures with the same self-etching bonding system.

Self-etching bonding systems are widely used in fiber post cementation. However, no clear guidelines are established for choosing pre- or co-curing procedures. We investigated the bond strength of fiber post cementation using pre-/co-curing methods in self-etching bonding systems and compared them with those of a self-adhesive system. Post spaces were prepared in 30 single-rooted premolars/canines, and the fiber posts were cemented in three ways (10 specimens per group): using a self-etching bonding system with either a pre-curing or simultaneous co-curing procedure (RelyX™ Ultimate; groups SE-pre and SE-co, respectively) and using a self-adhesive system (RelyX™ Unicem 2, group SA). Each specimen was embedded and sliced perpendicularly to the long axis into three 2.5-mm-thick sections. Microphotographs of the coronal and apical surfaces of each section were acquired, and push-out tests (1 mm/min) were performed. One-way analysis of variance was conducted on the data, followed by Tukey's honestly significant difference post hoc test. The bond strength in the whole root was not significantly different among the three groups. When independently evaluating each portion, group SE-co exhibited significantly lower coronal bond strength. The bond strength varied among root regions only in group SE-pre; the apical region had a significantly lower value. No cementation method is superior in all portions. Regarding pre-curing methods, clinicians must caution the fit between the post and post space, which may be affected by the pre-polymerized bond layer. The co-curing method used in a larger coronal cement space contributes to the poor bond strength. [ABSTRACT FROM AUTHOR]

Copyright of Journal of Dental Sciences is the property of Elsevier B.V. and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)