Influence of vulcanization factors on UV-A resistance of silicone rubber for outdoor insulators.

High temperature vulcanized silicone rubber (HTVSR) used outdoors is often deteriorated by ultraviolet (UV)-A radiation. UV-A resistance of HTVSR is related to network structures affected by vulcanization conditions (temperature, time, and pressure). To improve the UV-A resistance of HTVSR, an orthogonal experiment about vulcanization conditions was established. Mechanical properties, electrical properties, crosslink density, and Fourier transform infrared spectroscopy (FTIR) of a total of 747 HTVSR samples were measured during the UV-A aging process. Based on the change rates of the above properties, a comprehensive change degree index was proposed to assess the UV-A resistance. It was found that HTVSR vulcanized at 170°C, for 15 min, and under 12 MPa was endowed with excellent UV-A resistance due to the high crosslink degree, low content of —OH groups, and evenly dispersed fillers. They decreased the diffusion of oxygen and free radicals generated during the UV-A aging, the activity of silicone rubber to UV-A radiation, and the surface area of silicone rubber exposed to UV-A radiation. This statistical analysis result was verified by comparing HTVSR vulcanized under this condition with that vulcanized under other conditions in practice. This paper provides a potential approach to optimize UV-A resistance of HTVSR at the initial fabrication process. [ABSTRACT FROM AUTHOR]

Copyright of IEEE Transactions on Dielectrics & Electrical Insulation is the property of IEEE and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)