Effect of Dy and Nd on ZK10 alloy processed by hot extrusion.

About 0.6%Dy and 0.2%Nd are simultaneously added to ZK10 alloy processed by hot extrusion, and their effects are investigated. Obvious refined grains and weakened texture are observed after addition of Dy and Nd. Significantly improved mechanical performance with increase of 16% in yield strength and of 114% in ductility is obtained compared with ZK10 alloy. The strengthening effect is attributed to the grain refinement and solid solution, and the enhanced ductility results from the refined structure and weakened texture. Better optimization in mechanical performance with enhanced strengthening is generated, compared with the alloy with individual RE element addition. Combined addition of trace Dy and Nd throws light on the wide-range production and application of extruded ZK10 alloy. [ABSTRACT FROM PUBLISHER]

Copyright of Materials & Manufacturing Processes is the property of Taylor & Francis Ltd and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)