Effect of hydroquinone-induced iron reduction on the stability of scorodite and arsenic mobilization.

Scorodite precipitation is widely employed for the fixation of arsenic in hydrometallurgical industries. However, its stability in reducing environment is not yet fully understood. This work investigated the effect of hydroquinone-induced Fe(III) reduction on the stability of scorodite. The results showed that ≤ 3% (11.3 mg L − 1 ) arsenic and < 4% (11 mg L − 1 ) Fe(II) were released into solution after 72–90% of Fe(III) was reduced to Fe(II) at pH 4–8. This indicated that most of the reductive decomposition generated Fe(II) and As(V) were retained in the solid phases as secondary minerals. The XRD, ATR-FTIR, Raman, SEM-EDS and chemical analysis suggested that amorphous FeHAsO 4 ⋅ xH 2 O was very likely the major sink for arsenic immobilization. At pH 9, the scorodite decomposed completely resulting in ~ 19% (71.2 mg L − 1 ) arsenic and ~ 3% (8.2 mg L − 1 ) Fe(II) release and a residual solid of Fe/As ~ 1.2. Both amorphous ferrous arsenates and Fe(II, III) (hydr)oxides were probably responsible for the retention of arsenic in this case. The solubility of scorodite in terms of dissolved arsenic concentration upon iron reduction at pH 7–9 was significantly lower than that in oxic environment under the conditions of this work. [ABSTRACT FROM AUTHOR]

Copyright of Hydrometallurgy is the property of Elsevier B.V. and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)